40Cr paipu irin jẹ iru irin yika pẹlu apakan ṣofo ati pe ko si awọn isẹpo ni ayika. O jẹ ti paipu to lagbara ti o ṣofo nipasẹ perforation, ati lẹhinna ṣe ti yiyi gbona, yiyi tutu tabi iyaworan tutu. Ti a ṣe afiwe pẹlu irin yika ati irin miiran ti o lagbara, nigbati atunse ati agbara torsional jẹ kanna, iwuwo ti paipu irin jẹ fẹẹrẹfẹ, eyiti o jẹ iru apakan apakan ti irin-aje.
Ni ibamu si GB / T 3077-2008: kemikali tiwqn (ibi-ida,%) C 0.37 ~ 0.44, Si 0.17 ~ 0.37, Mn 0.50 ~ 0.80, cr0.80 ~ 1.10, Ni ≤ 0.30【 Mechanical-ini]
Apeere iwọn òfo (mm): 25
Alapapo otutu ti akọkọ quenching (℃): 850; Itura: Epo
Iwọn otutu alapapo keji (℃):
Iwọn otutu alapapo (℃): 520; Itura: omi, epo
Agbara fifẹ (σ b/MPa): ≧980
Aaye ikore (σ s/MPa): ≧785
Ilọsiwaju lẹhin fifọ (δ 5/%): ≧9
Idinku agbegbe (ψ/%): ≧45
Agbara gbigba ipa (aku2 / J): ≥ 47
Lile Brinell (hbs100 / 3000) (ti a ti mu tabi iwọn otutu ti o ga): ≤ 207
Awọn onipò irin ti GB ni Ilu China jẹ 40Cr, ohun elo DIN No. / ASTM Standard Irin No.. 5140, Japanese JIS boṣewa irin No.. scr440 (H) / scr440, American AISI / SAE / ASTM Standard Irin No.. 5140, okeere agbari fun Standardization ISO boṣewa irin No.. 41Cr4.
(isunmọ) ACM = 780 ℃
Awọn iwọn otutu 850 ~ 870 ℃, lile 179 ~ 229hbs.
Iwọn otutu jẹ 740 ~ 760 ℃, akoko idaduro jẹ 4 ~ 6h, ati lẹhinna iwọn otutu ti wa ni tutu si ≤ 600 ℃ ni itutu agbaiye ti 5 ~ 10 ℃ / h.
Lile ṣaaju itọju ≤ 217hbs, lile lẹhin rirọ ≤ 163hbs.
(670 ± 10) ℃ × 2H, iwọn otutu dide pẹlu ileru, (710 ± 10) ℃ × 2H, dara pẹlu ileru, (670 ± 10) ℃ × 2H, iwọn otutu dide pẹlu ileru, (710 ± 10) ℃ × 2H, lẹhinna dinku iwọn otutu pẹlu ileru, (670 ± 10) ℃ × 2H, iwọn otutu dide pẹlu ileru, (710 ± 10) ℃ × 2H, dara si isalẹ pẹlu ileru fun awọn iyipo 3, ati lẹhinna dara si isalẹ lati 550 ℃ fun itutu afẹfẹ. Lile lẹhin itọju jẹ 153hbs.
Quenching otutu 850 ℃± 10 ℃, epo itutu; Iwọn otutu otutu 520 ℃ ± 10 ℃, omi, epo ati itutu afẹfẹ.
Alabọde erogba modulated irin, tutu akori kú irin. Awọn irin ni o ni dede owo ati ki o rọrun processing. Lẹhin itọju ooru ti o yẹ, o le gba awọn lile lile, ṣiṣu ati yiya resistance. Normalizing le ṣe igbelaruge spheroidization tissu ati ilọsiwaju iṣẹ gige ti awọn ofo pẹlu lile ti o kere ju 160hbs. Tempered ni 550 ~ 570 ℃, irin naa ni awọn ohun-ini ẹrọ imọ-ẹrọ ti o dara julọ. Hardenability ti irin yii ga ju ti irin 45 lọ. O dara fun itọju líle dada bii pipana igbohunsafẹfẹ giga ati pipa ina.
Lẹhin quenching ati tempering, irin yii ni a lo lati ṣe iṣelọpọ awọn ẹya ẹrọ ti o ni ẹru alabọde ati iyara alabọde, gẹgẹ bi ọpa idari, ọpa idaji ẹhin ti ọkọ ayọkẹlẹ, jia, ọpa, alajerun, ọpa spline, apo aarin, ati bẹbẹ lọ lori ohun elo ẹrọ; Lẹhin quenching ati iwọn otutu otutu alabọde, o lo lati ṣe iṣelọpọ awọn ẹya ti o ni ẹru giga, ipa ati iyara alabọde, gẹgẹbi jia, ọpa akọkọ, rotor fifa epo, bulọọki sisun, kola, ati bẹbẹ lọ; Lẹhin quenching ati iwọn otutu otutu kekere, a lo lati ṣe awọn ẹya pẹlu ẹru iwuwo, ipa kekere, wọ resistance ati sisanra to lagbara ti o kere ju 25mm lori apakan, gẹgẹbi alajerun, ọpa akọkọ, ọpa, kola, ati bẹbẹ lọ; Lẹhin quenching ati tempering ati ki o ga-igbohunsafẹfẹ dada quenching, o ti wa ni lo lati lọpọ awọn ẹya ara pẹlu ga dada líle ati wọ resistance lai nla ikolu, gẹgẹ bi awọn jia, apo, ọpa, akọkọ ọpa, crankshaft, spindle, pin, pọ opa, dabaru, nut, àtọwọdá inlet, bbl Ni afikun, irin yii tun dara fun iṣelọpọ orisirisi awọn ẹya gbigbe ti a ṣe itọju nipasẹ carbonitriding, gẹgẹbi awọn jia ati awọn ọpa pẹlu iwọn ila opin nla ati lile iwọn otutu ti o dara.
Annealed, lile ≤ 207hbs. 40Cr rirọ modulus: rirọ modulus E (20 ℃) / MPA 200000 ~ 211700, rirẹ modulus G (20 ℃) 80800
Ilana piparẹ ti 40Cr
40Cr quenching, 850 ℃, epo itutu; Tempering 520 ℃, omi itutu agbaiye, epo itutu. Lile pipa dada ti paipu irin 40Cr jẹ hrc52-60, ati pe ina quenching le de ọdọ hrc48-55.
40Cr nitriding itọju
40Cr jẹ ti irin nitrided, ati awọn eroja rẹ jẹ iwunilori si nitriding. 40Cr le gba ti o ga dada líle lẹhin nitriding itọju, ati awọn ga líle lẹhin nitriding itọju le de ọdọ hra72 ~ 78, ie hrc43 ~ 55. Nitriding workpiece ilana ipa: forging annealing ti o ni inira machining quenching ati tempering pari machining wahala yiyọ ti o ni inira lilọ nitriding finishing lilọ tabi lilọ. Nitori Layer nitrided jẹ tinrin ati brittle, o nilo lati ni eto mojuto agbara-giga, nitorinaa o jẹ dandan lati gbe quenching ati itọju ooru tutu ni akọkọ lati gba sorbite tempered ati ilọsiwaju awọn ohun-ini ẹrọ ti mojuto ati didara ti mojuto. nitrided Layer. Nitriding rirọ jẹ nitriding lọwọ, ati nitriding gaasi jẹ lilo nigbagbogbo
40Cr alurinmorin
Ṣaaju ki o to 40Cr alurinmorin, san ifojusi si preheating lati se quench kiraki inu awọn weld nitori matrix ooru wọbia. O dara julọ lati ṣe deede ṣaaju alurinmorin.
Weldability ti 40Cr: o rọrun lati ya sọtọ nigba crystallization ati ki o jẹ kókó si crystallization kiraki (a irú ti gbona kiraki). O ti wa ni rọrun lati kiraki ni Crater ati concave apakan ninu awọn weld nigba alurinmorin. Pẹlu akoonu erogba giga, o rọrun lati gba eto lile (martensite) eyiti o ni itara pupọ si awọn dojuijako tutu lakoko itutu agbaiye iyara. Nigbati oṣuwọn itutu agbaiye ti agbegbe gbigbona ti o tobi, o rọrun lati dagba lile ati brittle carbon martensite giga ati ki o tẹ agbegbe ti o gbona ju.
1. Alurinmorin ti wa ni gbogbo ti gbe jade ni annealed (normalized) ipinle.
2. Ọna alurinmorin ko ni opin
3.Iwọn otutu alapapo le jẹ alekun ni deede pẹlu agbara laini nla. Ni gbogbogbo, iwọn otutu iṣaju ati iwọn otutu interlayer le jẹ iṣakoso laarin 250 ~ 300 ℃.
4. Ohun elo alurinmorin yoo rii daju pe akopọ ti irin ti a fi silẹ jẹ ipilẹ kanna bi ti irin ipilẹ, bii j107-cr.
5.Quenching ati tempering ooru itọju yoo wa ni ti gbe jade ni akoko lẹhin alurinmorin. Ti o ba soro lati gbe jade quenching ati tempering itọju ni akoko, agbedemeji annealing tabi dimu ni a otutu ti o ga ju preheating fun akoko kan ti akoko le ti wa ni ti gbe jade lati se imukuro tan kaakiri hydrogen ati ki o rọ awọn be. Fun awọn ọja pẹlu eto eka ati ọpọlọpọ awọn welds, annealing agbedemeji le ṣee ṣe lẹhin alurinmorin nọmba kan ti awọn welds.