42CrMo alloy irin pipe olupese atilẹyin ọja tita
Idi ti paipu irin alailẹgbẹ 42CrMo: irin pataki fun Afara jẹ “42CrMo”, irin pataki fun girder ọkọ ayọkẹlẹ jẹ “42CrMo”, ati irin pataki fun ọkọ oju omi titẹ jẹ “42CrMo”. Iru irin yii ṣe ilọsiwaju awọn ohun-ini ẹrọ ti irin nipasẹ ṣiṣatunṣe akoonu erogba (c). Nitorinaa, ni ibamu si akoonu erogba, iru irin yii le pin si: irin kekere erogba - akoonu erogba ni gbogbogbo kere ju 0.25%, bii 10 ati 20 irin; Irin erogba alabọde - akoonu erogba jẹ gbogbogbo laarin 0.25 ~ 0.60%, bii 35 ati 45 irin; Irin erogba giga - akoonu erogba ni gbogbogbo tobi ju 0.60%. Iru irin yii kii ṣe ni gbogbogbo ni iṣelọpọ awọn paipu irin. Irin 42CrMo jẹ irin agbara giga-giga pẹlu agbara giga ati lile, lile ti o dara, ko si iha tutu ti o han gbangba, opin rirẹ giga ati resistance ipa pupọ lẹhin piparẹ ati itọju iwọn otutu, ati lile ipa iwọn otutu to dara. Irin 42CrMo dara fun iṣelọpọ awọn apẹrẹ ṣiṣu nla ati alabọde ti o nilo agbara kan ati lile. Lile: annealed, 147 ~ 241hb, 42CrMo
Agbara fifẹ σ b (MPa): ≥1080(110)
Agbara ikore σ s (MPa): ≥930(95)
Ilọsiwaju δ 5 (%): ≥12
Idinku agbegbe ψ (%): ≥45
Agbara ipa Akv (J): ≥ 63
Iye to lagbara ikolu α kv (J/cm2): ≥78(8)
Lile: ≤ 217hb
Lati le ni ilọsiwaju igbesi aye iṣẹ ti ku si diẹ sii ju awọn akoko 800000, ọna lile ti quenching ati iwọn otutu iwọn otutu le ṣe imuse fun irin lile ti o ṣaju. Lakoko quenching, o yẹ ki o jẹ preheated ni 500-600 ℃ fun awọn wakati 2-4, lẹhinna tọju ni 850-880 ℃ fun akoko kan (o kere ju wakati 2), tutu ninu epo si 50-100 ℃ ati tutu nipasẹ afẹfẹ. Lile lẹhin quenching le de ọdọ 50-52hrc. Ni ibere lati yago fun wo inu, o yẹ ki o wa ni iwọn otutu 200 ℃ lẹsẹkẹsẹ. Lẹhin ti tempering, líle le wa ni muduro loke 48hrc. Ilana itọju iwẹ iyọ didoju ti 42CrMo irin. Layer carbide le ṣee gba nipasẹ itọju ibi iwẹ iyọ didoju ti irin 42CrMo.
1. Erogba vanadium yellow, awọn carburized Layer ni o ni aṣọ be, ti o dara lilọsiwaju ati iwapọ, aṣọ sisanra, iwapọ be, ga microhardness ati ki o ga yiya resistance, ati awọn dada líle, wọ resistance ati adhesion resistance ti wa ni gidigidi dara si.
2.Solubility ti VC ni austenite jẹ ti o ga ju pe ni ferrite. Pẹlu idinku iwọn otutu, VC n ṣafẹri lati ferrite, eyiti o jẹ ki alloy lagbara ati isọdọtun ọkà, ati Layer yellow fihan lile lile. Irin 42CrMo jẹ ti erogba giga ati irin chromium ledeburite giga, pẹlu akoonu carbide giga, ṣiṣe iṣiro nipa 20%, ati nigbagbogbo pin kaakiri lainidi ni igbanu tabi nẹtiwọọki, pẹlu ipinya pataki. Bibẹẹkọ, itọju ooru aṣa jẹ soro lati yi ipinya carbide pada, eyiti o ni ipa lori awọn ohun-ini ẹrọ ti irin ati igbesi aye iṣẹ ti ku. Apẹrẹ ati iwọn ti awọn carbides tun ni ipa nla lori awọn ohun-ini ti irin. Ni pataki, awọn carbide igun didasilẹ nla ni ipa pipin nla lori matrix irin ati nigbagbogbo di orisun ti fifọ rirẹ. Nitorinaa, o jẹ dandan lati yipada sisẹ ti irin aise ti yiyi, ni kikun fifun pa awọn eutectic carbides lati jẹ ki wọn jẹ itanran ati pinpin ni deede, ati pe ọna okun ti pin kaakiri iho tabi ti kii ṣe itọsọna, nitorinaa lati mu ilọsiwaju awọn ohun-ini ẹrọ iṣipopada ti irin. .
Lakoko ayederu, billet naa yoo binu ati fa lati awọn itọnisọna oriṣiriṣi fun ọpọlọpọ awọn akoko, ati pe o jẹ eke nipasẹ ọna “ina meji ati iwuwo kan”, iyẹn ni, billet yoo wa ni rọn ni ibẹrẹ ti ayederu lati yago fun fifọ. O le jẹ lilu pupọ ni iwọn otutu agbedemeji ti 980 ~ 1020 ℃ lati rii daju fifun pa awọn carbides. 42CrMo, irin ti ko ba eke, ati ojutu ri to ė refining itọju ti wa ni gba, ti o ni, Atẹle preheating ni nipa 500 ℃ ati 800 ℃ ati ri to ojutu itọju ni 1100 ~ 1150 ℃, Quenching pẹlu gbona epo tabi isothermal quenching, ga otutu tempering ni 750 ℃, alapapo ni 960 ℃ lẹhin machining ati itọju ooru ikẹhin lẹhin itutu agba epo tun le ṣatunṣe awọn carbides, awọn egbegbe ati awọn igun ati sọ awọn irugbin di mimọ.