35CrMo alloy irin pipe olupese awọn iranran atilẹyin ọja tita
35CrMo jẹ nọmba sipesifikesonu ti irin igbekalẹ alloy (alloy quenched ati irin tempered), eyiti o jẹ lilo ni akọkọ lati ṣe awọn ẹya pataki ni ọpọlọpọ awọn ẹrọ ti o ni ipa, atunse ati torsion ati fifuye giga. Koodu oni-nọmba ti iṣọkan ti 35CrMo alloy irin igbekale irin (alloy quenched ati tempered steel) jẹ a30352, ati pe boṣewa adari jẹ GB / t3077-2015
35 crmo
35CrMo (awọn abọ meji)
Italy: 35crmo4
NBN: 34crmo4
Sweden: 2234
Iwọn ojoojumọ: scm432 / sccrm3
O ti lo lati ṣe iṣelọpọ awọn ẹya pataki ni ọpọlọpọ awọn ẹrọ ti o ni ipa, atunse ati torsion ati ẹru giga, gẹgẹ bi jia egugun egugun, crankshaft, ọpá hammer, ọpá asopọ ati awọn ohun elo ti irin yiyi ọlọ, ọpa akọkọ ati axle ti ẹrọ turbine nya si, gbigbe engine awọn ẹya ara, ọpa ọkọ nla, perforator ni ẹrọ epo, awọn boluti igbomikana pẹlu iwọn otutu ti o ṣiṣẹ ni isalẹ ju 400 ℃, awọn eso pẹlu iwọn otutu ti o ṣiṣẹ ni isalẹ ju 510 ℃, Iwọn odi ti o nipọn ti o nipọn (iwọn otutu 450 ~ 500 ℃, ko si alabọde ibajẹ) ninu ẹrọ kemikali ; O tun le rọpo 40crni fun iṣelọpọ ọpa gbigbe fifuye giga, ẹrọ iyipo ẹrọ turbine, jia apakan nla, ọpa atilẹyin (opin ti o kere ju 500mm), ati bẹbẹ lọ; Awọn ohun elo ohun elo ilana, awọn paipu, awọn ohun elo alurinmorin, ati bẹbẹ lọ.
Ti a lo bi awọn ẹya igbekale pataki ti n ṣiṣẹ labẹ ẹru giga, gẹgẹbi awọn ẹya gbigbe ti awọn ọkọ ati awọn ẹrọ; Rotor, ọpa akọkọ, ọpa gbigbe ẹru iwuwo ati awọn apakan nla ti olupilẹṣẹ turbine nya si.
Erogba C: 0.32 ~ 0.40
Silikoni Si: 0.17 ~ 0.37
Mn: 0.40 ~ 0.70
Sulfur s: Allowable akoonu iṣẹku ≤ 0.035
Phosphorus P: Allowable akoonu iṣẹku ≤ 0.035
K: 0.80 ~ 1.10
Nickel: Allowable akoonu iṣẹku ≤ 0.30
Ejò Cu: Allowable akoonu iṣẹku ≤ 0.30
Mo: 0.15 ~ 0.25
Agbara fifẹ σ b (MPa): ≥985(100)
Agbara ikore σ s (MPa): ≥835(85)
Ilọsiwaju δ 5 (%): ≥12
Idinku agbegbe ψ (%): ≥45
Agbara ipa Akv (J): ≥ 63
Iye tokiki ikolu α kv (J/cm²): ≥78(8)
Lile: ≤ 229hb
Iwọn apẹẹrẹ: iwọn òfo apẹẹrẹ jẹ 25mm
Ooru itọju sipesifikesonu ati metallographic be
Ooru itọju sipesifikesonu: quenching 850 ℃, epo itutu; Tempering 550 ℃, omi itutu agbaiye, epo itutu.
Irin ite: 35CrMo
Apeere iwọn ofo / mm: 25
Ooru itọju | quenching | alapapo otutu / ℃ | akọkọ pa: 850
Ooru itọju | quenching | alapapo otutu / ℃ | keji pa: --
Ooru itọju | quenching | coolant: Epo
Ooru itọju | tempering | alapapo otutu / ℃: 550
Ooru itọju | tempering | coolant: omi, epo
Darí-ini | agbara fifẹ σ b/MPa|≥: 980
Darí-ini | ojuami ikore σ s/MPa|≥: 835
Darí-ini | elongation δ 5(%)|≥: 12
Darí-ini | isunki dada ψ(%)| ≥: 45
Darí-ini | ipa gbigba agbara Akv / J | ≥: 63
Ifijiṣẹ ipinle líle HBS | ≥: 229
Ifijiṣẹ ipo: ifijiṣẹ ni ooru itọju (normalizing, annealing tabi ga otutu tempering) tabi ti kii ooru itoju ipo, ati awọn ifijiṣẹ ipo yoo wa ni itọkasi ni awọn guide.